Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation at break		DIN 53504-S2	50 %
elongation at break	elongation at break	80℃水中21天	DIN 53504-S2	600 %
Shore hardness		DIN 53505	92 shoreA
compression set	室温	DIN 53517	25 %
Impact strength of cantilever beam gap	－30℃	DIN 53453	不破裂 KJ/m
Shore hardness		DIN 53505	42 Shore D
Tensile modulus		DIN 53504-S2	16 N/mm
compression set	70℃	DIN 53517	45
tensile strength	80℃水中21天	DIN 53504-S2	35 N/mm
Friction loss		DIN 53516	25 mm
Impact strength of cantilever beam gap	＋23℃	DIN 53453	不破裂 KJ/m
Tensile modulus	20%	DIN 53504-S2	4.5 N/mm
tensile strength		DIN 53504-S2	50 N/mm
tear strength		DIN 53515	65 N/mm
Tensile modulus	100%	DIN 53504-S2	8.5 N/mm
	Tensile modulus	100%	ASTM D412/ISO 527	4.5 Mpa/Psi
	Tensile modulus	Tensile modulus	300%	ASTM D412/ISO 527	8.5 Mpa/Psi
tensile strength		ASTM D412/ISO 527	50 Mpa/Psi
tear strength		ASTM D624/ISO 34	65 n/mm²
Shore hardness		ASTM D2240/ISO 868	92 Shore A
Shore hardness	Shore hardness		ASTM D2240/ISO 868	42 Shore D