برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون gloss ASTM D-523 93
other شرایط آزمون روش آزمون نتیجه آزمون purpose 建材及汽机车部品
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 1/4",23℃ ASTM D-256 25(4.6) kg-cm/cm(ft-lb/im) tensile strength 1/8“,6mm/min ASTM D-638 450(6380) kg/cm2(lb/in2) bending strength 1/4“,2.8mm/min ASTM D-790 660(9330) kg/cm2(lb/in2) Impact strength of cantilever beam gap ASTM D256/ISO 179 25 kg·cm/cm(J/M)ft·lb/in Impact strength of cantilever beam gap ASTM D256/ISO 179 45 kg·cm/cm(J/M)ft·lb/in tensile strength ASTM D638/ISO 527 420 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 550 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature 1/8“,50℃/hr ASTM D-1525 105(221) ℃(℉) Hot deformation temperature 1/4“,120℃/hr,Annealed ASTM D-648 95(203) ℃(℉) Hot deformation temperature HDT ASTM D648/ISO 75 95 ℃(℉) Vicat softening temperature ASTM D1525/ISO R306 105 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 200℃,10kg ASTM D-1238 4 g/10min density ASTM D792/ISO 1183 1.07 melt mass-flow rate ASTM D1238/ISO 1133 4 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.