برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون transmissivity Total ASTM D1003 91.0 % turbidity ASTM D1003 <1.0 %
impact performance شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength 23°C ASTM D4812 无断裂 Dart impact -40°C,EnergyatPeakLoad ASTM D3763 67.0 J Dart impact 0°C,EnergyatPeakLoad ASTM D3763 65.0 J Dart impact 23°C,EnergyatPeakLoad ASTM D3763 62.0 J
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus 23°C ASTM D638 1610 Mpa Tensile modulus 23°C ISO 527-2 1570 Mpa tensile strength Yield,23°C ASTMD638 45.0 Mpa tensile strength Break,23°C ASTM D638 52.0 Mpa tensile strength Break,23°C ISO 527-2 51.0 Mpa elongation Yield,23°C ASTMD638 7.0 % elongation Break,23°C ASTMD638 140 % Bending modulus 23°C ASTM D790 1520 Mpa Bending modulus 23°C ISO 178 1490 Mpa bending strength 23°C ISO 178 60.0 Mpa bending strength Yield,23°C ASTM D790 64.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed ASTM D648 101 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 85.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD ASTM D955 0.60 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale,23°C ASTM D785 110