Basic performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	220℃×10kg	ASTM D-238	8 g/10min
density	23℃	ASTM D-792	1.04 g/cm³
melt mass-flow rate	200℃×21.6kg	ASTM D-238	16 g/10min
melt mass-flow rate	melt mass-flow rate	200℃×5kg	ASTM D-1238	0.9 g/10min

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness		ASTM D-785	111 R scale
elongation at break		ASTM D-638	20 %
tensile strength	23℃	ASTM D-638	500 kg/cm2
bending strength	23℃	ASTM D-790	720 kg/cm2
Impact strength of cantilever beam gap	1/8in(3.2mm)23℃	ASTM D-256	14 kg.cm/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/4in(6.4mm) 23℃	ASTM D-256	12 kg.cm/cm
Flexural modulus	23℃	ASTM D-790	24000 kg/cm2

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat		ASTM D-1525	138(280) ℃（℉）
Heat distortion temperature	未退火，6.4mm 18.6kg/cm2，HDT	ASTM D-648	108(227) ℃（℉）
Heat distortion temperature	Heat distortion temperature	退火，6.4mm 18.6kg/cm2，HDT	ASTM D-648	131(268) ℃（℉）