physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	210℃/2.16 kg	ASTM D1238	10 to 25 g/10 min
Shrinkage rate	MD		0.30 - 0.50 %
melt mass-flow rate	210°C/2.16kg	ASTM D1238	14 g/10min
Shrinkage rate	MD		0.30-0.50 %
relative viscosity		内部方法	3.30

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Clarity			Transparent

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	屈服	ASTM D638	48.3 Mpa
elongation	断裂	ASTM D638	2.5 %
Flexural modulus		ASTM D790	3830 Mpa
bending strength		ASTM D790	82.7 Mpa
tensile strength	屈服	ASTM D638	62.1 Mpa
elongation	断裂	ASTM D638	3.5 %
Flexural modulus		ASTM D790	3550 Mpa
bending strength		ASTM D790	108 Mpa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Glass Transition Temperature	DSC	ASTM D3417	55.0 to 65.0 °C
Crystallization peak temperature	DSC	ASTM D3418	150 to 165 °C
Glass Transition Temperature		ASTM D3418	55.0to65.0 °C
Crystallization peak temperature	DSC	ASTM D3418	145to160 °C