برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength 23°C ASTM D4812 440 J/m Suspended wall beam without notch impact strength 23°C3 ISO 180/1U 28 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus --1 ASTM D638 7580 Mpa Tensile modulus -- ISO 527-2/1 7470 Mpa tensile strength Yield ASTM D638 91.0 Mpa tensile strength Yield ISO 527-2 93.0 Mpa tensile strength Break ASTM D638 91.0 Mpa tensile strength Break ISO 527-2 93.0 Mpa elongation Yield ASTM D638 2.1 % elongation Break ASTM D638 2.1 % Bending modulus -- ASTM D790 6200 Mpa Bending modulus -- ISO 178 6700 Mpa bending strength -- ASTM D790 137 Mpa bending strength -- ISO 178 142 Mpa Friction coefficient Dynamic ASTM D3702 0.35 Friction coefficient Static ASTM D3702 0.36 Wear factor ASTM D3702 9.9E+6 10^-8 mm³/N·m
injection شرایط آزمون روش آزمون نتیجه آزمون drying time 4.0 hr Suggested maximum moisture content 0.020 % Back pressure 0.200 to 0.300 Mpa Screw speed 30 to 60 rpm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion Flow : -40 to 40°C ASTM E831 4.1E-5 cm/cm/°C Linear coefficient of thermal expansion Across Flow : -40 to 40°C ASTM E831 6.3E-5 cm/cm/°C Linear coefficient of thermal expansion Across Flow : -40°C ISO 11359-2 6.3E-5 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.30 g/cm³ Shrinkage rate Flow : 24hr ASTM D955 0.30 - 0.50 % Shrinkage rate Across FlowFlow : 24hr ASTM D955 0.40 - 0.60 % Shrinkage rate 横向Flow : 24hr ISO 294-4 0.54 % Shrinkage rate Flow : 24hr ISO 294-4 0.43 %