physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Flow: 24 hours	24小时	ASTM D955	0.40to0.60 %
Water absorption rate	24hr,50%RH	ASTM D570	0.10 %
Lateral flow: 24 hours	横向, 24小时	ASTM D955	0.60to0.80 %
Vertical flow direction: 24 hours	垂直方向, 24小时	ISO 294-4	0.65 %
Flow direction: 24 hours	流动方向, 24小时	ISO 294-4	0.50 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Wear factor	Washer	ASTM D3702Modified	166 10^-10in^5-min/ft-lb-hr
bending strength		ISO 178	118 Mpa
--1		ASTM D638	4140 Mpa
fracture		ASTM D638	5.5 %
yield		ASTM D638	71.7 Mpa
yield	yield		ISO 527-2	71.0 Mpa
fracture		ASTM D638	67.6 Mpa
coefficient of friction	与自身-动态	ASTM D3702Modified	0.38
yield		ASTMD638	3.3 %
coefficient of friction	与自身-静态	ASTM D3702Modified	0.44
fracture		ISO 527-2	5.8 %
fracture	fracture		ISO 527-2	67.0 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
23°C		ASTM D4812	740 J/m
23°C	23°C		ISO 180/1U	49 kJ/m²
23°C,EnergyatPeakLoad		ASTM D3763	23.2 J
23°C		ASTM D256	140 J/m
23°C	23°C		ISO 180/1A	13 kJ/m²

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
0.45MPa, Unanealed, 64.0mm span		ISO 75-2/Bf	146 °C
1.8MPa, Unanealed, 3.20mm		ASTM D648	140 °C
Linear coefficient of thermal expansion	MD:-40到40°C	ASTME831	5.6E-05 cm/cm/°C
1.8MPa, Unanealed, 64.0mm span		ISO 75-2/Af	140 °C
Linear coefficient of thermal expansion	TD:-40到40°C	ASTME831	5.6E-05 cm/cm/°C
0.45MPa, Unanealed, 3.20mm		ASTM D648	145 °C