Impact strength of simply supported beam without notch
23°C
ISO 179
69 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
0.38mm
UL 94
V-0
UL flame retardant rating
0.75mm
UL 94
V-0
UL flame retardant rating
1.5mm
UL 94
V-0
UL flame retardant rating
3.0mm
UL 94
V-0
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
23°C
ISO 527-2
3770 Mpa
tensile strength
Yield,23°C
ISO 527-2
84.0 Mpa
Tensile strain
Yield,23°C
ISO 527-2
3.7 %
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
RTI Imp
3.0mm
UL 746
105 °C
RTI Str
0.38mm
UL 746
65.0 °C
RTI Str
0.75mm
UL 746
115 °C
RTI Str
1.5mm
UL 746
120 °C
RTI Str
3.0mm
UL 746
120 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
68.0 °C
Melting temperature
ISO 3146
243 °C
RTI Elec
0.38mm
UL 746
110 °C
RTI Elec
0.75mm
UL 746
120 °C
RTI Elec
1.5mm
UL 746
120 °C
RTI Elec
3.0mm
UL 746
120 °C
RTI Imp
0.38mm
UL 746
65.0 °C
RTI Imp
0.75mm
UL 746
105 °C
RTI Imp
1.5mm
UL 746
105 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Water absorption rate
Saturation,23°C
ISO 62
8.5 %
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
2.9 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Compared to the anti leakage trace index
IEC 60112
PLC 0