physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	12 g/10 min
Melt volume flow rate	300°C/1.2 kg	ISO 1133	10.0 cm3/10min
Shrinkage rate	流动 : 3.20 mm	内部方法	0.40 - 0.80 %
Shrinkage rate	Shrinkage rate	横向流动 : 3.20 mm	内部方法	0.40 - 0.80 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	L 计秤	ASTM D785	83
Rockwell hardness	Rockwell hardness	R 级	ASTM D785	117

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.50 mm	UL 94	V-2
	UL flame retardant rating	0.8 mm	UL 94	V-1
		UL flame retardant rating	1.0 mm	UL 94	V-0
			UL flame retardant rating	1.5 mm	UL 94	5VB
			UL flame retardant rating	UL flame retardant rating	3.1 mm	UL 94	5VA
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	850 °C
Limiting Oxygen Index		ISO 4589-2	39 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	--2	ASTM D638	2110 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2140 Mpa
tensile strength	屈服3	ASTM D638	56.0 Mpa
	tensile strength	屈服	ISO 527-2/50	57.0 Mpa
		tensile strength	断裂3	ASTM D638	62.0 Mpa
		tensile strength	tensile strength	断裂	ISO 527-2/50	60.0 Mpa
elongation	屈服3	ASTM D638	5.8 %
	elongation	屈服	ISO 527-2/50	5.6 %
		elongation	断裂3	ASTM D638	110 %
		elongation	elongation	断裂	ISO 527-2/50	110 %
Flexural modulus	50.0 mm 跨距4	ASTM D790	2190 Mpa
Flexural modulus	Flexural modulus	--5	ISO 178	2180 Mpa
bending strength	--5,6	ISO 178	86.0 Mpa
bending strength	bending strength	屈服, 50.0 mm 跨距4	ASTM D790	88.0 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	29 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	75 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	67.0 J

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface Resistivity		ASTM D257	> 1.0E+16 ohms
Volume resistivity		ASTM D257	> 1.0E+16 ohms·cm
dielectric strength	3.20 mm, in Oil	ASTM D149	13 KV/mm
dielectric constant	1.10 GHz	ASTM ES7-83	2.78
Dissipation Factor	1.10 GHz	ASTM ES7-83	6.0E-3

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			270 to 295 °C
Temperature in the middle of the barrel			280 to 305 °C
Temperature at the front of the material cylinder			295 to 315 °C
Spray nozzle temperature			290 to 310 °C
Processing (melt) temperature			295 to 315 °C
Temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45 MPa, 未退火, 3.20 mm，HDT	ASTM D648	134 °C
	Heat distortion temperature	0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距9，HDT	ISO 75-2/Be	131 °C
		Heat distortion temperature	1.8 MPa, 未退火, 3.20 mm，HDT	ASTM D648	118 °C
		Heat distortion temperature	Heat distortion temperature	1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9，HDT	ISO 75-2/Ae	117 °C
vicat	--	ISO 306/B50	136 °C
vicat	vicat	--	ISO 306/B120	138 °C
Linear coefficient of thermal expansion	流动 : -40 到 40°C	ASTM E831	6.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	流动 : 23 到 80°C	ISO 11359-2	7.4E-5 cm/cm/°C
		Linear coefficient of thermal expansion	横向 : -40 到 40°C	ASTM E831	7.3E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 23 到 80°C	ISO 11359-2	7.6E-5 cm/cm/°C