برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون turbidity ASTM D1003 0.40 %
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.6 mm UL 94 V-2
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D638 69.0 Mpa elongation Break ASTM D638 130 % Bending modulus ASTM D790 2250 Mpa bending strength Yield ASTM D790 93.0 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 120 °C drying time 3.0 to 5.0 hr Suggested maximum moisture content 0.020 % Temperature at the rear of the barrel 235 to 260 °C Temperature in the middle of the barrel 250 to 275 °C Temperature at the front of the material cylinder 265 to 290 °C Spray nozzle temperature 265 to 300 °C Processing (melt) temperature 265 to 300 °C Mold temperature 65 to 105 °C Back pressure 0.250 to 0.700 Mpa Screw speed 40 to 70 rpm Exhaust hole depth 0.020 to 0.080 mm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8 MPa, Unannealed ASTM D648 134 °C Linear coefficient of thermal expansion Flow ASTM D696 5.0E-5 - 7.0E-5 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 300°C/1.2 kg ASTM D1238 16 g/10 min Water absorption rate 24 hr, 23°C ASTM D570 0.15 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D257 4.0E+16 ohms·cm Dielectric strength ASTM D149 30 KV/mm Arc resistance ASTM D495 120 sec