برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Break, 23°C, 3.20 mm, Injection ASTM D638 196 Mpa elongation Break, 23°C, 3.20 mm, Injection ASTM D638 3.0 % Bending modulus 23°C, 3.20 mm, Injection ASTM D790 11800 Mpa bending strength 23°C, 3.20 mm, Injection ASTM D790 275 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 80 to 100 °C drying time 4.0 to 5.0 hr Temperature at the rear of the barrel 260 to 270 °C Temperature in the middle of the barrel 270 to 285 °C Temperature at the front of the material cylinder 270 to 290 °C Spray nozzle temperature 270 to 295 °C Processing (melt) temperature 270 to 295 °C Mold temperature 80 to 110 °C Back pressure 29.4 to 58.8 Mpa Screw speed 30 to 60 rpm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm, Injection ASTM D648 210 °C Melting temperature ASTM D3418 220 °C Linear coefficient of thermal expansion Flow ASTM D696 3.0E-5 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 23°C, 3.20 mm, Injection,Flow ASTM D955 0.30 - 0.70 % Water absorption rate 24 hr, 23°C ASTM D570 0.60 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity 23°C ASTM D257 1.0E+16 ohms·cm Dielectric strength 23°C, 1.00 mm ASTM D149 25 KV/mm Dielectric constant 23°C, 1 MHz ASTM D150 4.00
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale, 23°C, Injection ASTM D785 120