برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Charpy Notched Impact Strength 23°C ISO 179/1eA 2.3 kJ/m² Impact strength of cantilever beam gap 23°C6 ASTM D256 0.51 J/m Impact strength of cantilever beam gap 23°C ISO 180/1A 3.4 kJ/m² Dart impact 23°C, 3.18 mm ASTM D5420 102 J
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ISO 527-2/1 1460 Mpa tensile strength Yield2 ASTM D638 33.8 Mpa tensile strength Yield, 23°C ISO 527-2/50 31.9 Mpa Tensile strain Yield ISO 527-2/50 9.9 % Bending modulus 1% Secant 3 ASTM D790A 1340 Mpa Bending modulus 1% Secant 4 ASTM D790B 1570 Mpa Bending modulus --5 ISO 178 1360 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45 MPa, Unannealed ASTM D648 88.9 °C Hot deformation temperature 0.45 MPa, Unannealed ISO 75-2/Bf 76.4 °C Hot deformation temperature 0.45 MPa, Annealed ASTM D648 113 °C Hot deformation temperature 1.8 MPa, Unannealed ISO 75-2/Af 47.4 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D1505 0.900 g/cm³ melt mass-flow rate 230°C/2.16 kg ASTM D1238 13 g/10 min
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness ASTM D785 105 Shore hardness 15 sec ISO 868 69