Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	3.2mm	ASTM D-256	85 J/m
elongation at break	3.2mm	ASTM D-638	1.4 %
bending strength	3.2mm	ASTM D-790	177 Mpa
tensile strength	3.2mm	ASTM D-638	132 Mpa
Flexural modulus	3.2mm	ASTM D-790	15200 Mpa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	85 kg·cm/cm(J/M)ft·lb/in
elongation at break		ASTM D638/ISO 527	1.4 %
tensile strength		ASTM D638/ISO 527	132 kg/cm²(MPa)[Lb/in²]
Flexural modulus		ASTM D790/ISO 178	15200 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	177 kg/cm²(MPa)[Lb/in²]

Other performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Grade @ Thickness		UL 746-B	V-0
Thickness Tested		UL 94	1.5 mm

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792/ISO 1183	1.77

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Temperature range for molding			30-95 °C
RTI Imp	3.0mm	UL 746-B	220 °C
	RTI Imp	3.0mm	UL 746-B	240 °C
	RTI Imp	RTI Imp	1.0mm	UL 746-B	240 °C
Glass Transition Temperature		ASTM D-3418	120 °C
RTI Elec	3.0mm	UL 746-B	240 °C
RTI Imp	1.0mm	UL 746-B	210 °C
drying temperature			135 °C
melting temperature		ASTM D-3418	335 °C
RTI Elec	1.0mm	UL 746-B	240 °C
Heat distortion temperature	1.80MPa，HDT	ASTM D-648	272 °C
melting temperature			350-360 °C
Heat distortion temperature	HDT	ASTM D648/ISO 75	272 ℃（℉）
melting temperature			335 ℃（℉）