Impact strength of simply supported beam without notch
23℃
ISO 179 1eU
5.0 J/cm
Charpy Notched Impact Strength
低温-30℃
ISO 179 1eA
0.45 J/cm
Impact strength of simply supported beam without notch
低温-30℃
ISO 179 1eU
5.0 J/cm
Charpy Notched Impact Strength
23℃
ISO 179 1eA
0.5 J/cm
Tensile creep modulus
1 hour
ISO 899 part 1
1800 Mpa
Tensile creep modulus
1000 hours
ISO 899 part 1
1000 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Linear coefficient of thermal expansion
23-55℃ Longitudinal
ISO 11359 part 1/2
140 µm/m-℃
Melting temperature
DSC,10 K/min
ISO 3146 method C1b
166 °C
Hot deformation temperature
1.8MPa
ISO 75 part 1/2
84 °C
Vicat softening temperature
VST/B/50
ISO 306
140 °C
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dielectric constant
1 MHz
IEC 60250
3.80
Dielectric constant
低频100 Hz
IEC 60250
3.80
Dielectric strength
IEC 60243 part 1
35 KV/mm
Dissipation factor
1 MHz
IEC 60250
0.007
Dissipation factor
低频100 Hz
IEC 60250
0.002