Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	断裂, 3.20 mm	ASTM D638	113 Mpa
elongation	断裂, 3.20 mm	ASTM D638	2.0 %
Flexural modulus	3.20 mm	ASTM D790	9320 Mpa
bending strength	屈服, 3.20 mm	ASTM D790	186 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric strength	23°C, 1.00 mm	ASTM D149	31 KV/mm
Compared to the Leakage Tracking Index (CTI)	解决方案 A	IEC 60112	V

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 to 100 °C
drying time			3.0 to 5.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			270 to 290 °C
Temperature in the middle of the barrel			280 to 310 °C
Temperature at the front of the material cylinder			290 to 310 °C
Spray nozzle temperature			280 to 310 °C
Processing (melt) temperature			280 to 310 °C
Temperature			80 to 150 °C
screw speed			40 to 80 rpm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45 MPa, 未退火, 6.40 mm，HDT	ASTM D648	260 °C
Heat distortion temperature	Heat distortion temperature	1.8 MPa, 未退火, 6.40 mm，HDT	ASTM D648	230 °C