Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation at break		ASTM D412/ISO 527	700 %
tensile strength		ASTM D412/ISO 527	95 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	40
tear strength		ASTM D624/ISO 34	95 kN/m
Flexural modulus		ASTM D790/ISO 178	134 kg/cm²(MPa)[Lb/in²]
Poisson's ratio		ASTM E-132	0.45
Flexural modulus	-40C(-40F)	ASTM D-790 IB	172(25) MPa（kpsi）
Flexural modulus	Flexural modulus	100C(212F)	ASTM D-790 IB	28(4.1) MPa（kpsi）
Shore hardness		ASTM D-2240	40
Impact strength of cantilever beam gap	23C(73F),6.35mm(0.25in)	ASTM D-256-A	NB J/m(ft lb/in)
tear strength		ASTM D-1004	95(550) KN/m(lb/in)
elongation	断裂	ASTM D-638	700 %
tensile strength	张力 10%	ASTM D-638	3.5(0.5) MPa（kpsi）
Impact strength of cantilever beam gap	-40C(-40F),6.35mm(0.25in)	ASTM D-256-A	NB J/m(ft lb/in)
tensile strength	张力 5%	ASTM D-638	2.4(0.4) MPa（kpsi）
tensile strength	tensile strength	断裂	ASTM D-638	20(2.9) MPa（kpsi）
Flexural modulus	23C(73F)	ASTM D-790 IB	55(8.0) MPa（kpsi）

Other performance	روش آزمون	نتیجه آزمون
Thickness grade	UL 94	HB
Thickness testing	UL 94	1.56 mm
density	ASTM D-792	1.11

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D955	1.11 %

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melting temperature			193 ℃（℉）
vicat		ASTM D1525/ISO R306	134 ℃（℉）
Heat distortion temperature	0.45MPa(66psi)，HDT	ASTM D-648	55(131) ℃(°F)
vicat		ASTM D-1525-B	134(273) ℃(°F)
melting temperature		ASTM D-3418	193(379) ℃(°F)

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.