برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,TotalEnergy ASTM D3763 61.0 J Dart impact -30°C,TotalEnergy ASTM D3763 54.2 J
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus 50.0mmSpan ASTM D790 2340 Mpa elongation Break ASTM D638 150 % elongation Yield ASTM D638 5.0 % tensile strength Yield ASTM D638 56.5 Mpa Tensile modulus ASTM D638 2210 Mpa bending strength Yield,50.0mmSpan ASTM D790 86.2 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون thermal conductivity ASTMC177 0.20 W/m/K Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 107 °C Hot deformation temperature 0.45MPa,Unannealed,3.20mm ASTM D648 124 °C Linear coefficient of thermal expansion MD:-40to40°C ASTME831 7.2E-05 cm/cm/°C Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 110 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate Equilibrium,23°C ASTM D570 0.40 % Water absorption rate 24hr ASTM D570 0.10 % Shrinkage rate MD:3.20mm Internal Method 0.50-0.70 % melt mass-flow rate 260°C/5.0kg ASTM D1238 9.0 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.