Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
Initial weightlessness temperature	Air	内部方法	499 °C
Initial weightlessness temperature	Initial weightlessness temperature	Nitrogen	内部方法	499 °C

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	5030 Mpa
tensile strength		ASTM D638	100 Mpa
elongation	断裂	ASTM D638	2.2 %
Flexural modulus		ASTM D790	5000 Mpa
bending strength		ASTM D790	175 Mpa
Compression Modulus		ASTM D695	2960 Mpa
compressive strength		ASTM D695	207 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		ASTM D257	2E+16 ohms·cm
dielectric strength		ASTM D149	17 KV/mm
dielectric constant	1kHz	ASTM D150	3.40
dielectric constant	dielectric constant	10kHz	ASTM D150	3.40
Dissipation Factor	1kHz	ASTM D150	0.0
Dissipation Factor	Dissipation Factor	10kHz	ASTM D150	1E-03
arc resistance		ASTM D495	135 sec

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD：24到149°C	TMA	3.4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：199到299°C	TMA	7E-05 cm/cm/°C