برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون characteristic 低耐火性 purpose 电脑显示器、复印机、办公设备
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256/ISO 179 15 kg·cm/cm(J/M)ft·lb/in Impact strength of cantilever beam gap ASTM D256/ISO 179 17 kg·cm/cm(J/M)ft·lb/in bending strength ASTM D790/ISO 178 700 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 25000 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 102 tensile strength ASTM D638/ISO 527 460 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 45 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525/ISO R306 96 ℃(℉) Hot deformation temperature HDT ASTM D648/ISO 75 80 ℃(℉) Combustibility (rate) UL 94 V-2
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238/ISO 1133 55 g/10min melt mass-flow rate ASTM D1238/ISO 1133 5.5 g/10min Water absorption rate ASTM D570/ISO 62 0.3 % Shrinkage rate ASTM D955 0.4-0.7 % density ASTM D792/ISO 1183 1.07
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.