Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	---	ISO 180	5 kJ/m²
elongation at break	---	ISO 527	4 %
Charpy Notched Impact Strength	---	ISO 179-1993	5.5 kJ/m²
elongation at break	---	ISO 527	120 Mpa
Impact strength of simply supported beam without notch	---	ISO 179-1993	42 kJ/m²
Tensile modulus	---	ISO 527	6100 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity	---	IEC 93	10 E14.ohm.cm
Compared to the Leakage Traceability Index (CTI)	---	IEC 112	550 V
Surface Resistivity	---	IEC 93	0.1 E14.ohm
dielectric constant	1MHz	IEC 250	3.8 ---
Dielectric loss	1MHz	IEC 250	0.02 ---

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8MPa，HDT	ISO 179-1993	180 °C
combustibility	1.6mm	ISO 1210UL 94	HB V
Glow wire combustion index (GWFI)	1.6mm	IEC 695-2-1	650 °C
melting temperature	---	ISO 3146C	222 °C
Linear coefficient of thermal expansion	23℃-85℃	ISO 75-2	4.2 E-5/℃