برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break ASTM D638/ISO 527 20 % Impact strength of cantilever beam gap ASTM D256/ISO 179 20 kg·cm/cm(J/M)ft·lb/in Impact strength of cantilever beam gap ASTM D256/ISO 179 18 kg·cm/cm(J/M)ft·lb/in bending strength ASTM D790/ISO 178 680 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 23000 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 100 elongation ASTM D638/ISO 527 >5 % tensile strength ASTM D638/ISO 527 400 kg/cm²(MPa)[Lb/in²] Tensile modulus ASTM D638/ISO 527 20000 kg/cm²(MPa)[Lb/in²] Impact strength of cantilever beam gap ASTM D256/ISO 179 6 kg·cm/cm(J/M)ft·lb/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525/ISO R306 83 ℃(℉) Hot deformation temperature HDT ASTM D648/ISO 75 82 ℃(℉) Combustibility (rate) UL 94 V-0.5VA
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238/ISO 1133 11 g/10min Shrinkage rate ASTM D955 0.4-0.7 % density ASTM D792/ISO 1183 1.18
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.