برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation Break ISO 527-2/50 25 % Bending modulus --5 ASTM D790 1720 Mpa Bending modulus --6 ISO 178 2000 Mpa bending strength --5 ASTM D790 71.0 Mpa bending strength --6 ISO 178 71.0 Mpa tensile strength Yield4 ASTM D638 45.4 Mpa tensile strength Yield ISO 527-2/50 46.0 Mpa tensile strength Break ISO 527-2/50 34.0 Mpa elongation Break4 ASTM D638 40 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed ASTM D648 87.0 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 83.0 °C Hot deformation temperature 1.8MPa,Annealed ASTM D648 97.0 °C Hot deformation temperature 1.8MPa,Annealed ISO 75-2/A 100 °C Vicat softening temperature -- ASTM D15257 106 °C Vicat softening temperature -- ISO 306/A50 105 °C Vicat softening temperature -- ISO 306/B50 98.0 °C Linear coefficient of thermal expansion MD ISO 11359-2 8.8E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 200°C/5.0kg ASTM D1238 1.6 g/10min Melt Volume Flow Rate (MVR) 220°C/10.0kg ISO 1133 19.0 cm3/10min Shrinkage rate ISO 294-4 0.40-0.70 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale ASTM D785 113
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.