برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,TotalEnergy ASTM D3763 46.5 J
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.9mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D638 2250 Mpa tensile strength Yield ASTM D638 56.0 Mpa tensile strength Break ASTM D638 51.7 Mpa tensile strength Break3 ASTM D638 47.0 Mpa elongation Yield ASTM D638 5.7 % elongation Break ASTM D638 26 % elongation Break3 ASTM D638 33 % Bending modulus 50.0mmSpan4 ASTM D790 2330 Mpa Bending modulus -- ASTM D790 2340 Mpa bending strength ASTM D790 86.2 Mpa Friction coefficient Dynamic ASTM D3702Modified 0.20 Friction coefficient Static ASTM D3702Modified 0.14 Wear factor Washer ASTM D3702Modified 55.0 10^-10in^5-min/ft-lb-hr
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed,3.20mm ASTM D648 141 °C Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 130 °C Linear coefficient of thermal expansion MD:-30to30°C ASTM D696 7.1E-05 cm/cm/°C Linear coefficient of thermal expansion TD:-30to30°C ASTM D696 7.5E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:24hr ASTM D955 0.60-0.80 % Shrinkage rate TD:24hr ASTM D955 0.80-1.0 % Water absorption rate 24hr,50%RH ASTM D570 0.017 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.