thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat Deflection Temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	60.0 °C
melting temperature		ASTM D3418	220 °C
Linear coefficient of thermal expansion	MD	ASTM D696	8E-05 cm/cm/°C
Heat Deflection Temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	190 °C

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.8mm	UL 94	V-2

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	屈服,3.20mm	ASTM D638	76.5 Mpa
elongation	断裂,3.20mm	ASTM D638	15 %
flexural modulus	6.40mm	ASTM D790	3140 Mpa
bending strength	屈服,6.40mm	ASTM D790	108 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
volume resistivity	23°C	ASTM D257	1E+15 ohms·cm
dielectric strength	23°C,1.00mm	ASTM D149	21 KV/mm
dielectric constant	23°C,1MHz	ASTM D150	3.00
arc resistance		ASTM D495	80.0 sec
Compared to the Leakage Tracking Index (CTI)	解决方案A	IEC 60112	PLC 0

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
shrinkage rate	MD：23°C,3.20mm	ASTM D955	1.0-1.4 %
Water absorption rate	平衡	ASTM D570	1.3 %