physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD：24小时	ASTM D955	3.0E-3-5.0E-3 %
Water absorption rate	24hr,50%RH	ASTM D570	0.080 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.12 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ISO 180/1A	17 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	49 kJ/m²
Multi axis Instrumented Impact Energy		ISO 6603-2	7.32 J

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2/1	8710 Mpa
coefficient of friction	Dynamic	ASTM D3702Modified	0.0
coefficient of friction	coefficient of friction	Static	ASTM D3702Modified	0.0
Fracture bending strain		ISO 178	0.0 %
Wear factor	Ring	ASTM D3702Modified	0.00 10^-10in^5-min/ft-lb-hr
Wear factor	Wear factor	Washer	ASTM D3702Modified	0.00 10^-10in^5-min/ft-lb-hr

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火,3.20mm，HDT	ASTM D648	146 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火,64.0mm跨距，HDT	ISO 75-2/Af	144 °C