Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
GradientBarTackTemperature			127 °C
Opening Hours		ASTM D4497-94	<5.0 sec
T-shaped peel strength	AluminumFoil	ASTM D1876	500.0 N/m
T-shaped peel strength	T-shaped peel strength	MylarFilm	ASTM D1876	1500.0 N/m

Filling analysis	شرایط آزمون	روش آزمون	نتیجه آزمون
melt viscosity	204°C	ASTM D1084	72.0 Pa·s
Brookfield viscosity	15%T.S.inCyclohexanone:23°C		3.70 Pa·s
Brookfield viscosity	Brookfield viscosity	15%T.S.inTHF:23°C		0.900 Pa·s

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	--	ASTM D638	31.0 Mpa
	tensile strength	100%应变	ASTM D638	4.80 Mpa
	tensile strength	tensile strength	300%应变	ASTM D638	9.00 Mpa
elongation	断裂,0.762mm	ASTM D638	530 %

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	100%应变	ASTM D412	4.80 Mpa
	tensile strength	300%应变	ASTM D412	9.00 Mpa
	tensile strength	tensile strength	断裂	ASTM D412	31.0 Mpa
elongation	断裂	ASTM D412	530 %

Thermal performance	روش آزمون	نتیجه آزمون
Glass Transition Temperature	DSC	-38.0 °C
vicat	ASTM D1525	71.0 °C
RingandBall SoftningPoint	ASTME28-92	174 °C