برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5 mm UL 94 V-0 UL flame retardant rating 3.0 mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield, 23°C, 3.20 mm, Injection ASTM D638 118 Mpa Bending modulus 23°C, 3.20 mm, Injection ASTM D790 6860 Mpa bending strength 23°C, 3.20 mm, Injection ASTM D790 177 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 100 to 200 °C drying time 3.0 to 5.0 hr Suggested maximum moisture content 0.020 % Temperature at the rear of the barrel 270 to 300 °C Temperature in the middle of the barrel 280 to 310 °C Temperature at the front of the material cylinder 290 to 330 °C Spray nozzle temperature 290 to 330 °C Processing (melt) temperature 300 to 340 °C Mold temperature 90 to 120 °C Back pressure 0.981 to 3.92 Mpa Screw speed 40 to 70 rpm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm, Injection ASTM D648 142 °C RTI Elec UL 746 120 °C RTI Imp UL 746 90.0 °C RTI UL 746 105 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 300°C/1.2 kg ASTM D1238 5.0 g/10 min Shrinkage rate 23°C, 3.20 mm, Injection,Flow ASTM D955 0.10 - 0.30 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale, 23°C, Injection ASTM D785 120