برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength 23°C ASTM D638 150 Mpa Elongation at Break 23°C ASTM D638 1.0 % Tensile modulus 23°C ASTM D638 18500 Mpa Tensile modulus 泊松比 7.58 0.34 bending strength 23°C ASTM D790 230 Mpa Bending modulus 23°C ASTM D790 17500 Mpa Impact strength of cantilever beam gap 23°C ASTM D256 75 J/m Friction coefficient 动态 ASTM D3702 0.35 Friction coefficient 静态 ASTM D3702 0.35
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.80MPaUnannealed ASTM D648 265 °C Linear coefficient of thermal expansion MD ASTM D696 1.7E-05 cm/cm/°C Linear coefficient of thermal expansion TD ASTM D696 1.7E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD ASTM D995 0.25 % Shrinkage rate TD ASTM D995 1.00 % Water absorption rate (23°C,24hr) ASTM D570 0.02 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric constant 23°C ASTM D150 5.0 1MHz Dissipation factor 23°C ASTM D150 8E-03 1MHz Dissipation factor 耐电弧性 ASTM D495 180 S Dissipation factor 相对漏电起痕指数 ASTM D3638 250 V Volume resistivity ASTM D257 1E+16 Ω.cm Dielectric strength 1.60mm ASTM D149 16 KV/mm
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness ASTM D785 100 M(Scale) Rockwell hardness ASTM D785 121 R
flame retardant performance شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL -94 V-0 0.40mm UL flame retardant rating UL -94 V-0 0.80mm