برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D-638 37.2 Mpa tensile strength Break ASTM D-638 32.4 Mpa elongation at yield ASTM D-638 2.6 % Elongation at Break ASTM D-638 21 % Bending modulus ASTM D-790 2200 Mpa bending strength ASTM D-790 62.1 Mpa Impact strength of cantilever beam gap 3.18mm ASTM D-256 58.7 J/m Suspended wall beam without notch impact strength 3.18mm ASTM D-256 843 J/m Tensile modulus ASTM D-638 2130 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed ASTM D-648 91.7 °C Hot deformation temperature 1.80MPa,Unannealed ASTM D-648 89.4 °C Linear coefficient of thermal expansion Flow ASTM E-831 0.000095 cm/cm/℃ Linear coefficient of thermal expansion Transverse ASTM E-831 0.000095 cm/cm/℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate Flow,24hr ASTM D-955 0.50-0.70 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.