برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength 23°C ISO 527-2 52 Mpa Elongation at Break 23°C ISO 527-2 >50 % Tensile modulus 23°C ISO 527-2 2200 Mpa Impact strength of cantilever beam gap 23°C ISO 180/1A 45 kJ/m² Impact strength of cantilever beam gap -30°C ISO 180/1A 35 kJ/m²
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPaUnannealed ISO 75-2/Bf 124 °C Hot deformation temperature 1.80MPaAnnealed ISO 75-2/Af 103 °C Vicat softening temperature ISO 306/B50 119 °C Linear coefficient of thermal expansion MD ISO 11359-2 8E-05 cm/cm/°C Linear coefficient of thermal expansion TD ISO 11359-2 8.5E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD2.0mm ISO 294-4 0.75 % Shrinkage rate TD2.0mm ISO 294-4 0.75 % Water absorption rate (23°C,24hr) ISO 62 1.00 % Water absorption rate (23°C,50RH) ISO 62 0.20 % melt mass-flow rate 260℃/5.0Kg ISO 1133 15 cm3/10min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity IEC 60093 1E+15 Ω.cm Surface resistivity IEC 60093 1E+15 Ω.cm
flame retardant performance شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL -94 HB 0.85mm UL flame retardant rating UL -94 HB 1.50mm UL flame retardant rating UL -94 HB 3.00mm