برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength ASTM D638/ISO 527 70 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 94 Bending modulus ASTM D790/ISO 178 3040 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 108 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 120 R Wear resistance ASTM D1044 13 tensile strength ASTM D638 70 Mpa Elongation at Break ASTM D638 30 % bending strength ASTM D790 108 Mpa Bending modulus ASTM D790 3040 Mpa Impact strength of cantilever beam gap ASTM D256 49 J/m Rockwell hardness ASTM D785 94 M
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Combustibility (rate) UL 94 HB Hot deformation temperature HDT ASTM D648/ISO 75 136 ℃(℉) melt mass-flow rate ASTM D1238 39 g/10min Linear coefficient of thermal expansion 10 Hot deformation temperature 1.82MPa ASTM D648 136 °C Hot deformation temperature 0.45MPa ASTM D648 172 °C UL flame retardant rating UL 94 HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.42 melt mass-flow rate ASTM D1238/ISO 1133 39 g/10min Water absorption rate ASTM D570/ISO 62 0.2 % Water absorption rate ASTM D570 0.2 % Shrinkage rate Flow 1.7-2.1 % Shrinkage rate Across Flow 1.7-2.1 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.