Basic performance	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.41 g/cm
melt mass-flow rate	190℃/2.16kg	ISO 1133	2.2 cm
Shrinkage rate	Across flow	ISO 294-4	1.8 %
Shrinkage rate	Shrinkage rate	flow	ISO 294-4	2.2 %
Water absorption rate	Equilibrium,23℃,50%rh	ISO 62	0.2 %
Water absorption rate	Water absorption rate	Saturation,23℃	ISO 62	0.75 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2/1A/1	2500 MPa
tensile strength	Yield	ISO 527-2/1A/50	62 MPa
Tensile strain	Yield	ISO 527-2/1A/50	12 %
Flexural modulus	23℃	ISO 178	2400 MPa
Impact strength of simply supported beam without notch	23℃	ISO 179/1eA	8.5 KJ/m
Impact strength of cantilever beam gap	23℃	ISO 180/1A	7.6 KJ/m

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat		ISO 306/B50	161 ℃
melting temperature	DSC	ISO 11357	166 ℃
Linear coefficient of thermal expansion	flow	ISO 11359-2	0.00012 cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Transverse	ISO 11359-2	0.00012 cm/cm/℃
Heat distortion temperature	1.8MPa,Unannealed，HDT	ISO 75-2/A	93 ℃