Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C	ISO 527-2	2810 Mpa
tensile strength	屈服,23°C	ISO 527-2	62.0 Mpa
Tensile strain	屈服,23°C	ISO 527-2	10 %
Nominal tensile fracture strain	23°C	ISO 527-2	25 %
Flexural modulus	23°C	ISO 178	2340 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface Resistivity		IEC 60093	1E+13 ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
dielectric strength		IEC 60243-1	40 KV/mm
dielectric constant	100Hz	IEC 60250	3.80
dielectric constant	dielectric constant	1MHz	IEC 60250	3.80
Dissipation Factor	100Hz	IEC 60250	1E-03
Dissipation Factor	Dissipation Factor	1MHz	IEC 60250	5E-03
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	151 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	96.0 °C
melting temperature		ISO 3146	167 °C
RTI Elec	1.5mm	UL 746	105 °C
RTI Elec	RTI Elec	3.0mm	UL 746	105 °C
RTI Imp	1.5mm	UL 746	90.0 °C
RTI Imp	RTI Imp	3.0mm	UL 746	90.0 °C
RTI Str	1.5mm	UL 746	90.0 °C
RTI Str	RTI Str	3.0mm	UL 746	105 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.