برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Break,23°C ASTM D638 47.0 Mpa elongation Break,23°C ASTM D638 9.0 % Bending modulus 23°C,3.00mm,48.0mmSpan ASTM D790 2300 Mpa bending strength 23°C,3.00mm,48.0mmSpan ASTM D790 45.0 Mpa Friction coefficient Dynamic Internal Method 0.17 Wear amount Internal Method 220 10^-8mm³/N·m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed ASTM D648 91.0 °C Vicat softening temperature ASTM D15256 130 °C Linear coefficient of thermal expansion MD ASTM D696 1.2E-04 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/10.0kg JISK7210 7.0 g/10min Spiral flow length Internal Method 33.0 CM Shrinkage rate MD:2.00mm Internal Method 1.5 % Shrinkage rate TD:2.00mm Internal Method 1.3 % Water absorption rate 24hr ASTM D570 <0.010 % limiting pv value Internal Method >0.50 MPa·m/s
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D257 1.0E+17-1.0E+18 ohms·cm Dielectric strength ASTM D149 60 KV/mm Dielectric constant 23°C ASTM D150 2.50 Dissipation factor 1MHz ASTM D150 1.0E-4到2.0E-4
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale ASTM D785 63
Supplementary Information شرایط آزمون روش آزمون نتیجه آزمون HeatGenerationTemperature Internal Method 75 °C