Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength		ASTM D256/ISO 179	16 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	10 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	70 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	60 kg·cm/cm(J/M)ft·lb/in
elongation at break		ASTM D638/ISO 527	4 %
Tensile modulus		ASTM D638/ISO 527	200-500 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	160-100 kg/cm²(MPa)[Lb/in²]
Flexural modulus		ASTM D790/ISO 178	3000 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	250 kg/cm²(MPa)[Lb/in²]

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate		ASTM D955	0.13-0.70 %
melt mass-flow rate		ASTM D1238/ISO 1133	11 g/10min

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Combustibility (rate)		UL 94	<50
Heat distortion temperature	HDT	ASTM D648/ISO 75	-190 ℃（℉）
Heat distortion temperature	Heat distortion temperature	HDT	ASTM D648/ISO 75	-210 ℃（℉）
vicat		ASTM D1525/ISO R306	>200 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.2 mm/mm.℃