برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 0.75 mm UL 94 V-0 UL flame retardant rating 1.5 mm UL 94 V-0 UL flame retardant rating 3.0 mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ISO 527-2/5 48.0 Mpa Tensile strain Break ISO 527-2/5 52 % Bending modulus ISO 178 3670 Mpa bending strength ISO 178 89.0 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 80 to 100 °C drying time 3.0 to 4.0 hr Suggested maximum moisture content 0.020 % Temperature at the rear of the barrel 260 to 270 °C Temperature in the middle of the barrel 270 to 290 °C Temperature at the front of the material cylinder 290 to 300 °C Spray nozzle temperature 270 to 290 °C Processing (melt) temperature 260 to 300 °C Mold temperature 60 to 80 °C Back pressure 0.981 to 3.92 Mpa Screw speed < 80 rpm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45 MPa, Unannealed, 4.00 mm ISO 75-2/B 104 °C Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm ISO 75-2/A 94.0 °C Vicat softening temperature ISO 306/B50 109 °C RTI Elec UL 746 80.0 °C RTI Imp UL 746 80.0 °C RTI UL 746 80.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 250°C/2.16 kg ISO 1133 1.8 g/10 min melt mass-flow rate 260°C/5.0 kg ISO 1133 11 g/10 min