برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Charpy Notched Impact Strength 23°C ISO 179/1eA 35 kJ/m² Impact strength of cantilever beam gap 23°C ISO 180/1A 30 kJ/m² Impact strength of cantilever beam gap -30°C ISO 180/1A 10 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength ISO 178 95.0 Mpa Bending modulus ISO 178 3100 Mpa Tensile strain Break ISO 527-2/5 100 % Tensile strain Yield ISO 527-2/5 4.2 % tensile strength Break ISO 527-2/5 58.0 Mpa tensile strength Yield ISO 527-2/5 55.0 Mpa Tensile modulus ISO 527-2/1 3200 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion TD:-40to40°C ISO 11359-2 7E-05 cm/cm/°C Linear coefficient of thermal expansion MD:-40to40°C ISO 11359-2 6E-05 cm/cm/°C Vicat softening temperature -- ISO 306/B120 137 °C Vicat softening temperature -- ISO 306/B50 135 °C Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan ISO 75-2/Af 118 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:3.20mm Internal Method 0.40-0.60 % Melt Volume Flow Rate (MVR) 265°C/5.0kg ISO 1133 10.0 cm3/10min Water absorption rate Equilibrium,23°C,50%RH ISO 62 0.10 % Water absorption rate Saturation,23°C ISO 62 0.40 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.