physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD	ISO 294-4	1.7 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.9 %
Water absorption rate	饱和,23°C	ISO 62	0.75 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.20 %
density		ASTM D792	1.41 g/cm³
density	density		ISO 1183	1.41 g/cm³
Melt volume flow rate	190°C/2.16kg	ISO 1133	8.00 cm3/10min
Shrinkage rate	MD	ASTM D955	2.2 %
Shrinkage rate	Shrinkage rate	TD	ASTM D955	1.8 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2/1A/1	2700 Mpa
tensile strength	屈服,23°C	ASTM D638	60.7 Mpa
tensile strength	tensile strength	屈服	ISO 527-2/1A/50	64.0 Mpa
Tensile strain	屈服	ISO 527-2/1A/50	9.0 %
Flexural modulus	23°C	ISO 178	2470 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.7 kJ/m²

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	155 °C
	Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	110 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	91.0 °C
melting temperature		ASTM D3418	165 °C
melting temperature	melting temperature		ISO 11357-3	165 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04 cm/cm/°C