برگه داده فنی مقایسه

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	256 °C
melting temperature		ISO 3146	260 °C
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	262 °C

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C	ISO 179	13 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	15 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	85 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	95 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180	14 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	17 kJ/m²

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.57 g/cm³
shrinkage rate	TD	ISO 294-4	1.0 %
shrinkage rate	shrinkage rate	MD	ISO 294-4	0.40 %
Water absorption rate	饱和,23°C	ISO 62	4.0 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	1.2 %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C	ISO 527-2	17000 Mpa
tensile strength	断裂,23°C	ISO 527-2	240 Mpa
Tensile strain	断裂,23°C	ISO 527-2	2.5 %
flexural modulus	23°C	ISO 178	15300 Mpa
bending strength	23°C	ISO 178	360 Mpa

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.