برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Instrumented impact 23℃ ASTM D3763 506 ISO527-2/1 Impact strength of cantilever beam gap 23℃ ASTM D256 68 cm-kgf/cm Bending modulus ASTM D790 20300 kgf/cm tensile strength Break ASTM D638 400 kgf/cm tensile strength Yield ASTM D638 490 kgf/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 260°C/5.0 kgf ASTM D1238 23 g/10min Relative Heat Index (RTI) Mech w/o impact UL 746B ℃ Relative Heat Index (RTI) Mech w/impact UL 746B 85 ℃ Relative Heat Index (RTI) Elec UL 746B ℃ Linear coefficient of thermal expansion -40℃to 40℃, xflow ASTM E 831 8.64E-05 1/℃ Linear coefficient of thermal expansion -40℃to 40℃, flow ASTM E 831 7.92E-05 1/℃ Hot deformation temperature 1.8Mpa,Unannealed ASTM D648 85 ℃ Hot deformation temperature 0.45 Mpa,Unannealed ASTM D648 126 ℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate xflow, 3.2 mm % SABIC Method 1.2 - 1.4 Shrinkage rate flow, 3.2 mm % SABIC Method 1.2 - 1.4
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون High voltage arc tracing rate UL 746A PLC Code Compared to the Leakage Traceability Index (CTI) UL 746A PLC_2 Hot wire ignition UL 746A UL flame retardant rating UL 94 2.48 mm UL flame retardant rating UL 94 1.49 mm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.