برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength ASTM D-638 460 kg/cm2 Bending modulus ASTM D-790 22000 kg/cm2 Bending modulus ASTM D-790 750 kg/cm2 Rockwell hardness R-Scale ASTM D-785 104 Elongation at Break ASTM D-638 25 % impact elasticity Notched1/4" ASTM D-256 16 kgcm/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Burning rate 1/8" UL -94 HB Burning rate 1/16" UL -94 HB Hot deformation temperature Unannealed18.5kg/cm2,1/2" ASTM D-648 103 °C Burning rate 1/8" IEC 707 FH3-33 mm/min Vicat softening temperature 1.000g ASTM D-1525 125 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.004-0.007 mm/mm melt mass-flow rate 220℃/10kg ASTM D-1238 6 g/10min density ASTM D-792 1.05
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون High arc combustion index UL -746A PLC 0 Compared to the anti leakage trace index UL -746A PLCCode Hot wire ignition UL -746A PLC 5 Arc resistance ASTM D-495 PLC_6 High voltage arc tracing rate UL -746A PLC 2
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.