برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ASTM D790 20300 kgf/cm Impact strength of cantilever beam gap 23℃ ASTM D256 68 cm-kgf/cm Instrumented impact 23℃ ASTM D3763 506 ISO527-2/1 tensile strength Yield ASTM D638 490 kgf/cm tensile strength Break ASTM D638 400 kgf/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45 Mpa,Unannealed ASTM D648 126 ℃ Hot deformation temperature 1.8Mpa,Unannealed ASTM D648 85 ℃ Linear coefficient of thermal expansion -40℃to 40℃, flow ASTM E 831 7.92E-05 1/℃ Linear coefficient of thermal expansion -40℃to 40℃, xflow ASTM E 831 8.64E-05 1/℃ Relative Heat Index (RTI) Elec UL 746B ℃ Relative Heat Index (RTI) Mech w/impact UL 746B 85 ℃ Relative Heat Index (RTI) Mech w/o impact UL 746B ℃ melt mass-flow rate 260°C/5.0 kgf ASTM D1238 23 g/10min
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate flow, 3.2 mm % SABIC Method 1.2 - 1.4 Shrinkage rate xflow, 3.2 mm % SABIC Method 1.2 - 1.4
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Hot wire ignition UL 746A High voltage arc tracing rate UL 746A PLC Code Compared to the Leakage Traceability Index (CTI) UL 746A PLC_2 UL flame retardant rating UL 94 1.49 mm UL flame retardant rating UL 94 2.48 mm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.