Impact strength of simply supported beam without notch
ISO 179
NoBreak
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
1.8mm
UL 94
5VB
UL flame retardant rating
1.5mm
UL 94
V-0
UL flame retardant rating
1.0mm
UL 94
V-1
UL flame retardant rating
0.75mm
UL 94
V-2
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
bending strength
ISO 178
94.0 Mpa
Bending modulus
ISO 178
3200 Mpa
Tensile strain
Break
ISO 527-2/50
50 %
Tensile strain
Yield
ISO 527-2/50
2.0 %
tensile strength
Break
ISO 527-2/50
46.0 Mpa
tensile strength
Yield
ISO 527-2/50
62.0 Mpa
Tensile modulus
ISO 527-2/1
3300 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
93.0 °C
Linear coefficient of thermal expansion
TD
ISO 11359-2
7E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD
ISO 11359-2
6E-05 cm/cm/°C
Vicat softening temperature
ISO 306/B50
96.0 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
83.0 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD:4.00mm
Internal Method
0.40-0.60 %
Shrinkage rate
TD:4.00mm
Internal Method
0.40-0.60 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface resistivity
IEC 60093
1E+16 ohms