برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 0.800mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield,23°C ASTM D638 62.0 Mpa elongation Break,23°C ASTM D638 40 % Bending modulus 23°C ASTM D790 2650 Mpa bending strength 23°C ASTM D790 91.0 Mpa shear strength 2.00mm ASTM D732 55.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed ASTM D648 158 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 110 °C Hot deformation temperature Melting Temperature ASTM D648 165 °C Linear coefficient of thermal expansion MD:20to80°C ASTM D696 1.3E-04 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238 27 g/10min Shrinkage rate MD:3.00mm ASTM D955 2.0 % Water absorption rate Equilibrium,23°C,60%RH ASTM D570 0.22 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D257 1E+16 ohms Volume resistivity ASTM D257 1E+14 ohms·cm Dielectric strength ASTM D149 19 KV/mm Dielectric constant 1MHz ASTM D150 3.70 Dissipation factor 1MHz ASTM D150 7E-03
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ASTM D785 80