برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون characteristic 高光泽高流动
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 200℃,3.8kg ASTM D-1238 7.9 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break ASTM D638/ISO 527 42 % Impact strength of cantilever beam gap ASTM D256/ISO 179 30 kg·cm/cm(J/M)ft·lb/in elongation ASTM D638/ISO 527 3 % tensile strength ASTM D638/ISO 527 46 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 44 % elongation at yield 1/8",5mm/min ASTM D-638 3 % Impact strength of cantilever beam gap 23°C ASTM D-256 30 kJ/m² Elongation at Break 1/8",5mm/min ASTM D-638 42 % tensile strength 1/8",5mm/min,Break ASTM D-638 44 Mpa tensile strength Yield,1/8",5mm/min ASTM D-638 46 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525/ISO R306 95 ℃(℉) Vicat softening temperature 1/8",50℃/hr,120℃/10hr ASTM D-1525 95 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238/ISO 1133 7.9 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.