برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate g/10 min ASTM D-1238 15
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap Notch t3.2mm ASTM D-256 5.0 Kgf.cm/cm Elongation at Break t2mm ASTM D-732 670 Kgf/cm elongation 23℃ ASTM D-638 4 % Impact strength of cantilever beam gap t3.2mm S type ASTM D-1822 55 Kgf.cm/cm Rockwell hardness M scale ASTM D-785 M96 Bending modulus 23℃ ASTM D-790 7.60 bending strength 23℃ ASTM D-790 1430 Kgf/cm tensile strength 23℃ ASTM D-638 900 Kgf/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Combustibility t0.8mm UL 94 HB Linear coefficient of thermal expansion 20℃-80℃ ASTM D-696 3.5 Hot deformation temperature 18.6kgf/cm2 ASTM D-648 159 °C Hot deformation temperature 4.6kgf/cm2 ASTM D-648 163 °C Melting temperature 10℃/min DSC Method 165 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 23℃,60%RH ASTM D-570 0.23 % Shrinkage rate //方向 0.9 % filler content High %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D-257 1×10 Ω Volume resistivity ASTM D-257 1×10 Ω.cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.