Basic performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	23℃and50%RH	ISO 62	0.3 %
Water absorption rate	Water absorption rate	饱和23℃	ISO 62	0.8 %
melt mass-flow rate	16cm	ISO 1133	20.64 g/10min
density		ISO 1183	1.29 g/cm

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile creep modulus	1000 hours	ISO 899 part 1	400 Mpa
ball-indentation hardness	30秒数值	ISO 2039 part 1	35 Mpa
Tensile modulus	1mm/min	ISO 527 part 1/2	900 Mpa
Flexural modulus		ISO 178	800 Mpa
Charpy Notched Impact Strength	-30℃	ISO 179 1eA	0.9 J/cm
Charpy Notched Impact Strength	Charpy Notched Impact Strength	低温23℃	ISO 179 1eA	1.20 J/cm
permeability	deformation damage, 60x60x3mm	ISO 6603	15 mm
Tensile creep modulus	1 hour	ISO 899 part 1	700 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric constant	1 MHz	IEC 60250	5.30
dielectric constant	dielectric constant	低频100 Hz	IEC 60250	5.30
dielectric strength		IEC 60243 part 1	28 KV/mm
Dissipation Factor	1 MHz	IEC 60250	250
Dissipation Factor	Dissipation Factor	低频100 Hz	IEC 60250	300

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	23-55℃ Longitudinal	ISO 11359 part 1/2	120 µm/m-℃
Heat distortion temperature	1.8MPa，HDT	ISO 75 part 1/2	55 °C
vicat	VST/B/50	ISO 306	60 °C