physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD：3.2 mm流动	内部方法	0.5 - 0.7 %
Shrinkage rate	Shrinkage rate	TD：3.2 mmTransverse	内部方法	0.5 - 0.7 %
melt mass-flow rate	260℃，5.0kg260℃/5.0 kgf	ASTM D1238	13.5 g/10min

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	屈服，50 mm/min屈服，50mm/min	ASTM D638	53 Mpa
tensile strength	tensile strength	断裂，50 mm/minBreak，51mm/min	ASTM D638	55 Mpa
Tensile strain Tensile strain 50mm/min	屈服，50 mm/minYield	ASTM D638	5 %
Tensile strain Tensile strain 51mm/min	断裂，50 mm/minBreak	ASTM D638	120 %
Tensile modulus	50 mm/min50 mm / min	ASTM D638	2240 Mpa
bending strength	屈服，1.30 mm/min，50 mm跨度屈服，1.3 mm/min，50mm跨距	ASTM D790	86 Mpa
Flexural modulus	1.30 mm/min，50 mm跨距1.3 mm/min，50mm跨距	ASTM D790	2270 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23℃23°C	ASTM D256	680 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃-30°C	ASTM D256	500 J/m
Instrumented impact	23℃23°C	ASTM D 3763	51 J
Instrumented impact	Instrumented impact	-30℃-30°C	ASTM D 3763	57 J

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat		ASTM D1525	126 °C
Heat distortion temperature	3.2mm3.2mm，HDT	ASTM D 648	129 °C
Heat distortion temperature	Heat distortion temperature	6.4mm6.4mm，HDT	ASTM D 648	110 °C
Linear expansion coefficient, -40 ℃ to 40 ℃,	流动流动	GB 1040	0.000080 1/℃
Linear expansion coefficient, -40 ℃ to 41 ℃,	横向Transverse	GB 1040	0.000080 1/℃