برگه داده فنی مقایسهOther performance شرایط آزمون روش آزمون نتیجه آزمون High voltage arc tracing rate UL 746A PLC 0 High arc combustion index UL 746A PLC 0 Hot wire ignition UL 746A PLC 5 Arc resistance ASTM D-495 PLC_5 Compared to the anti leakage trace index UL 746A PLC 5
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-scale ASTM D-785 119 bending strength 15mm/min ASTM D-790 850 kg/cm tensile strength 50mm/min ASTM D638 450 kg/cm Impact strength of cantilever beam gap Notched 1/8" ASTM D-256 1.5 kg.cm/cm elongation 50mm/min ASTM D-638 4 % Bending modulus 15mm/min ASTM D-790 32000 kg/cm Impact strength of cantilever beam gap Notched 1/4" ASTM D-256 1.1 kg.cm/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Combustibility 1/8" UL 94 HB Vicat softening temperature 1000g ASTM D-1525 98 °C Combustibility 1/8" IEC 707 FH3-28 mm/min Hot deformation temperature Unannealed 18.5kg/cm ASTM D-648 82 °C Combustibility 1/16" UL 94 HB melt mass-flow rate 220℃/5Kg ASTM D-1238 9 g/10min
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.4-0.8 % density ASTM D-792 1.05
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.