برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break ASTM D638/ISO 527 1.3 % bending strength ASTM D790/ISO 178 205 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 15500 kg/cm²(MPa)[Lb/in²] tensile strength ASTM D638/ISO 527 153 kg/cm²(MPa)[Lb/in²] bending strength ISO 178 205 Mpa Bending modulus ISO 178 15500 Mpa Tensile strain Break ISO 527-2 1.3 % tensile strength ISO 527-2 153 Mpa Charpy Notched Impact Strength ISO 179/1eA 6.5 KJ/m Bending modulus ISO 178 15500 Mpa bending strength ISO 178 205 Mpa tensile strength ISO 527-1/-2 153 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Combustibility (rate) UL 94 HB Linear coefficient of thermal expansion MD:23to55°C Internal Method 2E-05 cm/cm/°C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 197 °C Linear coefficient of thermal expansion TD:23to55°C Internal Method 4E-05 cm/cm/°C UL flame retardant rating UL 94 HB Hot deformation temperature 1.8Mpa ISO 75-1/-2 197 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.73 Water absorption rate 23°C,24hr ISO 62 0.10 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity IEC 60093 6E+15 ohms·cm
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ISO 2039-2 100
Supplementary Information شرایط آزمون روش آزمون نتیجه آزمون ColourNumber ED3002